In the paper there is considered a new paper of plasma carbonization with the use of a graphite coating consisting of graphite, liquid glass and others. A procedure of coating production and the fulfillment of the experiment on coating and melting are shown. A new mechanism of carbon diffusion from coating into metal under the influence of plasma electric arc is offered. The character of surface micro-relief changes after carbonization is analyzed. When using the mentioned method of carbonization it is possible to increase micro-hardness of steel St3 4-5 times (up to 12000 MPa). The depth of a carbonized layer is within the limits of 50-200 µm (in the mode without surface melting) and 300 - 3000µm (in the mode of surface melting). It is shown that the application of liquid glass at the coating formation has a positive effect on surface roughness with the increase of liquid glass quantity roughness decreases.
plasma carbonization, paste, carbonization, diffusion, micro-hardness, micro-relief, roughness.
1. Balanovsky, А.Е. Metal Surface Plasma Strengthening. - Irkutsk: Publishing House of IrSTU, 2006. - pp. 180.
2. Grigoriyants, А.G. Laser technologies in mechanical engineering // Science Intensive Technologies in Mechanical Engineering. - 2011. - № 2(02). - pp. 14-22.
3. Chudina, О.V. Combined Methods of Steel Surface Strengthening with Laser Heating Use. Theory and Technology. - М.: MARI (STU), 2003. - pp. 248.
4. Balanovsky, А.Е. Plasma technologies in industry: state and outlooks //Blank Production in Mechanical Engineering. - 2007. - № 6. - pp. 9-14.
5. Skripkin, А.А., Netsvetaev, V.А., Shcherbakov, V.Е., Minenko, N.Yu. Manufacturing heat-resistant layers of steel 20 using plasma heating // Welding Engineering. - 1992. - № 11. - pp. 15-17.
6. Vu Van Guy., Balanovsky А.Е. Steam conducting plasma carbonization in solid phase on MULTIPLAZ 3500 plant// Innovation in Science. - 2015. - № 51-1. - pp. 95-102.
7. Losinskaya, А.А. Formation of high-carbon layers on steel and their hardening using power electronic beam led out in atmosphere // Promising Sciences, - 2013. - № 10 (49). - pp. 7-10.
8. Gal N.R., Rutkov Е.V., Tontegode А.Ya. Carbon Diffusion between Volume and Surface (100) of Molybdenum / / ZhTF. - 2002. Vol.72. - №4. - pp. 113-119.
9. Balanovsky, А.Е. Possibilities of digital visualization of heating and metal melting at arc discharge with non-consumable electrode // Welding Engineering. - 2016. - № 6. - pp. 31-40.
10. Samotugin, S.S., Solyanik, N.Kh., Puiko, А.V. Tool steel properties at plasma strengthening with surface melting // Welding Engineering. - 1994. - № 11. - pp. 20-24.