THE EFFECT OF HEAT TREATMENT TEMPERATURE ON THE MECHANICAL PROPERTIES OF COPPER M1.
Rubrics: MECHANICAL ENGINEERING AND TRANSPORT
Authors:
2.
Bryanskiy gosudarstvennyy tehnicheskiy universitet
(professor)
3.
Bryansk State Technical University
Type:
Article
Pages:
from 94
to 97
Status:
Published
Received:
02.12.2016
Accepted:
02.12.2016
Published:
02.12.2016
Language:
Russian
Keywords:
copper M1, flat specimen, tensile test, mechanical properties, tensile strength, relative residual elongation, temperature of heat treatment.
Abstract (English):
Tensile tests of specimens made from solid copper M1 had been conducted. Samples were subjected to heat treatment by heating to temperatures of 200 to 900°C and were cooled in water or air. Values of tensile strength and relative residual elongation were defined. The condi-tions under which solid copper acquires the properties of soft copper installed.
Tensile tests of specimens made from solid copper M1 had been conducted. Samples were subjected to heat treatment by heating to temperatures of 200 to 900°C and were cooled in water or air. Values of tensile strength and relative residual elongation were defined. The condi-tions under which solid copper acquires the properties of soft copper installed.