SCIENCE INTENSIVE TECHNOLOGY OF BURR FORMATION DECREASE AT PULSE LASER CUTTING OF SHEET MATERIAL
Authors:
Type:
Article
Pages:
from 43
to 48
Status:
Published
Received:
19.01.2016
Accepted:
08.02.2016
Published:
08.02.2016
Language:
Russian
Keywords:
аmount of burr, ultrasonic vibrations, cutting width, laser beam, gas pressure, cutting speed.
Abstract (English):
Conditions are revealed and means are offered for minimizing burr formation at cutting of sheet material made of titanium alloy BT1-0 and steel 12X18H10T. The influence of imposing of mechanical vibrations in ultrasound range on burr formation was investigated and the possibility of reducing the amount of burr with ultrasonic influence was showed. The influence of wetting of a lower edge of molten metal on a cutting quality was investigated, the possibility of reducing the burr amount using coating was showed. The influence of pressure of an auxiliary gas on reducing the amount of burr was investigated and importance of this parameter was confirmed. The results allow 30-60 % reduction in the amount of burr under otherwise equal conditions.
Conditions are revealed and means are offered for minimizing burr formation at cutting of sheet material made of titanium alloy BT1-0 and steel 12X18H10T. The influence of imposing of mechanical vibrations in ultrasound range on burr formation was investigated and the possibility of reducing the amount of burr with ultrasonic influence was showed. The influence of wetting of a lower edge of molten metal on a cutting quality was investigated, the possibility of reducing the burr amount using coating was showed. The influence of pressure of an auxiliary gas on reducing the amount of burr was investigated and importance of this parameter was confirmed. The results allow 30-60 % reduction in the amount of burr under otherwise equal conditions.
Keywords:
аmount of burr, ultrasonic vibrations, cutting width, laser beam, gas pressure, cutting speed.
аmount of burr, ultrasonic vibrations, cutting width, laser beam, gas pressure, cutting speed.
1. Kochergin S.A., Morgunov Yu.А., Saushkin B.P. Fea-tures of formation of burr under pulsed laser cutting of thin-walled workpieces. STIN. 2015, no. 10. Pp. 33-36.
2. Ershov G.S, Chernyakov V.A. The structure and properties of liquid and solid metals. Moscow: Metallurgy, 1978. 248 p.
3. Kukhling Kh. Handbook of physics. Moscow: Mir, 1982. 520 p.